K93600 Alloy vs. ASTM B628 Ag-Cu
K93600 alloy belongs to the iron alloys classification, while ASTM B628 Ag-Cu belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is ASTM B628 Ag-Cu.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
83 |
Elongation at Break, % | 5.0 to 35 | |
1.1 to 17 |
Shear Strength, MPa | 320 to 380 | |
210 to 430 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
350 to 760 |
Thermal Properties
Melting Onset (Solidus), °C | 1430 | |
780 |
Specific Heat Capacity, J/kg-K | 520 | |
280 |
Thermal Expansion, µm/m-K | 7.3 | |
19 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
84 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
75 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
10 |
Common Calculations
Stiffness to Weight: Axial, points | 9.4 | |
4.6 |
Stiffness to Weight: Bending, points | 21 | |
14 |
Strength to Weight: Axial, points | 16 to 28 | |
9.5 to 21 |
Strength to Weight: Bending, points | 17 to 24 | |
11 to 18 |
Thermal Shock Resistance, points | 34 to 57 | |
16 to 34 |