K93600 Alloy vs. EN 1.0038 Steel
Both K93600 alloy and EN 1.0038 steel are iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.0038 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
190 |
Elongation at Break, % | 5.0 to 35 | |
23 to 25 |
Shear Strength, MPa | 320 to 380 | |
240 to 270 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
380 to 430 |
Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
200 to 220 |
Thermal Properties
Maximum Temperature: Mechanical, °C | 440 | |
400 |
Melting Onset (Solidus), °C | 1430 | |
1420 |
Specific Heat Capacity, J/kg-K | 520 | |
470 |
Thermal Conductivity, W/m-K | 13 | |
49 |
Thermal Expansion, µm/m-K | 7.3 | |
12 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
7.2 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
8.3 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
7.8 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
72 to 88 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
110 to 130 |
Stiffness to Weight: Axial, points | 9.4 | |
13 |
Stiffness to Weight: Bending, points | 21 | |
24 |
Strength to Weight: Axial, points | 16 to 28 | |
13 to 15 |
Strength to Weight: Bending, points | 17 to 24 | |
15 to 16 |
Thermal Diffusivity, mm2/s | 3.1 | |
13 |
Thermal Shock Resistance, points | 34 to 57 | |
12 to 13 |