K93600 Alloy vs. EN 1.4596 Stainless Steel
Both K93600 alloy and EN 1.4596 stainless steel are iron alloys. There are 12 material properties with values for both materials. Properties with values for just one material (20, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is EN 1.4596 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
| 1030 to 1600 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 440 | |
| 790 |
| Melting Onset (Solidus), °C | 1430 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 520 | |
| 470 |
| Thermal Expansion, µm/m-K | 7.3 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.1 | |
| 7.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.4 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 16 to 28 | |
| 36 to 56 |
| Strength to Weight: Bending, points | 17 to 24 | |
| 29 to 39 |
| Thermal Shock Resistance, points | 34 to 57 | |
| 35 to 54 |