K93600 Alloy vs. Monel 400
K93600 alloy belongs to the iron alloys classification, while Monel 400 belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is K93600 alloy and the bottom bar is Monel 400.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 140 | |
160 |
Elongation at Break, % | 5.0 to 35 | |
20 to 40 |
Shear Strength, MPa | 320 to 380 | |
370 to 490 |
Tensile Strength: Ultimate (UTS), MPa | 480 to 810 | |
540 to 780 |
Tensile Strength: Yield (Proof), MPa | 280 to 750 | |
210 to 590 |
Thermal Properties
Curie Temperature, °C | 250 | |
40 |
Maximum Temperature: Mechanical, °C | 440 | |
1000 |
Melting Onset (Solidus), °C | 1430 | |
1300 |
Specific Heat Capacity, J/kg-K | 520 | |
430 |
Thermal Conductivity, W/m-K | 13 | |
23 |
Thermal Expansion, µm/m-K | 7.3 | |
14 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
3.3 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.4 | |
3.4 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.1 | |
8.9 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 21 to 280 | |
140 to 180 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 280 to 2050 | |
140 to 1080 |
Stiffness to Weight: Axial, points | 9.4 | |
10 |
Stiffness to Weight: Bending, points | 21 | |
21 |
Strength to Weight: Axial, points | 16 to 28 | |
17 to 25 |
Strength to Weight: Bending, points | 17 to 24 | |
17 to 21 |
Thermal Diffusivity, mm2/s | 3.1 | |
6.1 |
Thermal Shock Resistance, points | 34 to 57 | |
17 to 25 |