K94200 Alloy vs. EN 1.4596 Stainless Steel
Both K94200 alloy and EN 1.4596 stainless steel are iron alloys. There are 13 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is K94200 alloy and the bottom bar is EN 1.4596 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 140 | |
| 200 |
| Poisson's Ratio | 0.34 | |
| 0.28 |
| Shear Modulus, GPa | 54 | |
| 76 |
| Tensile Strength: Ultimate (UTS), MPa | 500 to 710 | |
| 1030 to 1600 |
Thermal Properties
| Melting Onset (Solidus), °C | 1440 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 500 | |
| 470 |
| Thermal Expansion, µm/m-K | 5.0 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 9.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 17 to 24 | |
| 36 to 56 |
| Strength to Weight: Bending, points | 17 to 22 | |
| 29 to 39 |
| Thermal Shock Resistance, points | 49 to 70 | |
| 35 to 54 |