N06200 Nickel vs. R60704 Alloy

N06200 nickel belongs to the nickel alloys classification, while R60704 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is N06200 nickel and the bottom bar is R60704 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
97
Elongation at Break, % 51
16
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 84
36
Tensile Strength: Ultimate (UTS), MPa 780
470
Tensile Strength: Yield (Proof), MPa 320
270

Thermal Properties

Latent Heat of Fusion, J/g 330
240
Specific Heat Capacity, J/kg-K 430
270
Thermal Conductivity, W/m-K 9.1
22
Thermal Expansion, µm/m-K 12
6.0

Otherwise Unclassified Properties

Density, g/cm3 8.7
6.7
Embodied Water, L/kg 310
460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 320
64
Resilience: Unit (Modulus of Resilience), kJ/m3 240
370
Stiffness to Weight: Axial, points 14
8.1
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 25
20
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 2.4
12
Thermal Shock Resistance, points 21
58

Alloy Composition

Aluminum (Al), % 0 to 0.5
0
Carbon (C), % 0 to 0.010
0 to 0.050
Chromium (Cr), % 22 to 24
0.2 to 0.4
Cobalt (Co), % 0 to 2.0
0
Copper (Cu), % 1.3 to 1.9
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 0 to 3.0
0.2 to 0.4
Manganese (Mn), % 0 to 0.010
0
Molybdenum (Mo), % 15 to 17
0
Nickel (Ni), % 51 to 61.7
0
Nitrogen (N), % 0
0 to 0.025
Oxygen (O), % 0
0 to 0.18
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.080
0
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
1.0 to 2.0
Zirconium (Zr), % 0
93 to 98.8