N06250 Nickel vs. SAE-AISI S5 Steel

N06250 nickel belongs to the nickel alloys classification, while SAE-AISI S5 steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is N06250 nickel and the bottom bar is SAE-AISI S5 steel.

UNS N06250 Nickel Alloy SAE-AISI S5 (T41905) Shock-Resisting Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		210
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.29
Poisson's Ratio		0.29

Shear Modulus, GPa		82
Shear Modulus, GPa		72

Tensile Strength: Ultimate (UTS), MPa		710
Tensile Strength: Ultimate (UTS), MPa		680 to 1940

Thermal Properties

Latent Heat of Fusion, J/g		320
Latent Heat of Fusion, J/g		280

Melting Completion (Liquidus), °C		1490
Melting Completion (Liquidus), °C		1440

Melting Onset (Solidus), °C		1440
Melting Onset (Solidus), °C		1400

Specific Heat Capacity, J/kg-K		440
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		13
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		55
Base Metal Price, % relative		3.1

Density, g/cm³		8.6
Density, g/cm³		7.7

Embodied Carbon, kg CO₂/kg material		10
Embodied Carbon, kg CO₂/kg material		2.1

Embodied Energy, MJ/kg		140
Embodied Energy, MJ/kg		29

Embodied Water, L/kg		270
Embodied Water, L/kg		51

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		23
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		23
Strength to Weight: Axial, points		25 to 70

Strength to Weight: Bending, points		21
Strength to Weight: Bending, points		22 to 45

Thermal Shock Resistance, points		19
Thermal Shock Resistance, points		23 to 65

Alloy Composition

Carbon (C), %		0 to 0.020
Carbon (C), %		0.5 to 0.65

Chromium (Cr), %		20 to 23
Chromium (Cr), %		0 to 0.5

Copper (Cu), %		0.25 to 1.3
Copper (Cu), %		0 to 0.25

Iron (Fe), %		7.4 to 19.4
Iron (Fe), %		93.6 to 97

Manganese (Mn), %		0 to 1.0
Manganese (Mn), %		0.6 to 1.0

Molybdenum (Mo), %		10.1 to 12
Molybdenum (Mo), %		0.2 to 1.4

Nickel (Ni), %		50 to 54
Nickel (Ni), %		0

Phosphorus (P), %		0 to 0.030
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 0.090
Silicon (Si), %		1.8 to 2.3

Sulfur (S), %		0 to 0.0050
Sulfur (S), %		0 to 0.030

Tungsten (W), %		0.25 to 1.3
Tungsten (W), %		0

Vanadium (V), %		0
Vanadium (V), %		0 to 0.35