N07041 Nickel vs. AISI 410 Stainless Steel
N07041 nickel belongs to the nickel alloys classification, while AISI 410 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.
For each property being compared, the top bar is N07041 nickel and the bottom bar is AISI 410 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 | |
| 16 to 22 |
| Fatigue Strength, MPa | 540 | |
| 190 to 350 |
| Shear Strength, MPa | 850 | |
| 330 to 470 |
| Tensile Strength: Ultimate (UTS), MPa | 1400 | |
| 520 to 770 |
| Tensile Strength: Yield (Proof), MPa | 1050 | |
| 290 to 580 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1480 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Conductivity, W/m-K | 11 | |
| 30 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.2 | |
| 7.7 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 | |
| 97 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 2510 | |
| 210 to 860 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 47 | |
| 19 to 28 |
| Strength to Weight: Bending, points | 34 | |
| 19 to 24 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 8.1 |
| Thermal Shock Resistance, points | 38 | |
| 18 to 26 |