N07041 Nickel vs. EN 1.4594 Stainless Steel

N07041 nickel belongs to the nickel alloys classification, while EN 1.4594 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is N07041 nickel and the bottom bar is EN 1.4594 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 220
200
Elongation at Break, % 14
11 to 17
Fatigue Strength, MPa 540
490 to 620
Shear Strength, MPa 850
620 to 700
Tensile Strength: Ultimate (UTS), MPa 1400
1020 to 1170
Tensile Strength: Yield (Proof), MPa 1050
810 to 1140

Thermal Properties

Melting Onset (Solidus), °C 1320
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 11
16
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Density, g/cm3 8.2
7.9

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180
110 to 190
Resilience: Unit (Modulus of Resilience), kJ/m3 2510
1660 to 3320
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 47
36 to 41
Strength to Weight: Bending, points 34
29 to 31
Thermal Diffusivity, mm2/s 3.0
4.4
Thermal Shock Resistance, points 38
34 to 39