N07716 Nickel vs. EN 1.4832 Stainless Steel

N07716 nickel belongs to the nickel alloys classification, while EN 1.4832 stainless steel belongs to the iron alloys. They have 40% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N07716 nickel and the bottom bar is EN 1.4832 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
11
Fatigue Strength, MPa 690
140
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 860
510
Tensile Strength: Yield (Proof), MPa 350
260

Thermal Properties

Latent Heat of Fusion, J/g 320
310
Maximum Temperature: Mechanical, °C 980
950
Melting Completion (Liquidus), °C 1480
1400
Melting Onset (Solidus), °C 1430
1360
Specific Heat Capacity, J/kg-K 440
480
Thermal Conductivity, W/m-K 11
14
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 75
19
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 13
3.6
Embodied Energy, MJ/kg 190
51
Embodied Water, L/kg 280
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
48
Resilience: Unit (Modulus of Resilience), kJ/m3 300
170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 28
18
Strength to Weight: Bending, points 24
18
Thermal Diffusivity, mm2/s 2.8
3.7
Thermal Shock Resistance, points 24
12

Alloy Composition

Aluminum (Al), % 0 to 0.35
0
Carbon (C), % 0 to 0.030
0.15 to 0.35
Chromium (Cr), % 19 to 22
19 to 21
Iron (Fe), % 0 to 11.3
58.6 to 67.4
Manganese (Mn), % 0 to 0.2
0 to 2.0
Molybdenum (Mo), % 7.0 to 9.5
0 to 0.5
Nickel (Ni), % 59 to 63
13 to 15
Niobium (Nb), % 2.8 to 4.0
0
Phosphorus (P), % 0 to 0.015
0 to 0.040
Silicon (Si), % 0 to 0.2
0.5 to 2.5
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 1.0 to 1.6
0