N08024 Nickel vs. AWS E430
N08024 nickel belongs to the nickel alloys classification, while AWS E430 belongs to the iron alloys. They have 51% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is N08024 nickel and the bottom bar is AWS E430.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 34 | |
| 23 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 79 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 280 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1440 |
| Melting Onset (Solidus), °C | 1380 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 480 |
| Thermal Conductivity, W/m-K | 12 | |
| 25 |
| Thermal Expansion, µm/m-K | 15 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.6 | |
| 2.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.8 | |
| 3.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 41 | |
| 9.0 |
| Density, g/cm3 | 8.2 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 7.2 | |
| 2.2 |
| Embodied Energy, MJ/kg | 99 | |
| 31 |
| Embodied Water, L/kg | 230 | |
| 120 |
Common Calculations
| PREN (Pitting Resistance) | 38 | |
| 18 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 21 | |
| 18 |
| Strength to Weight: Bending, points | 20 | |
| 18 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 6.7 |
| Thermal Shock Resistance, points | 15 | |
| 13 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0 to 0.1 |
| Chromium (Cr), % | 22.5 to 25 | |
| 15 to 18 |
| Copper (Cu), % | 0.5 to 1.5 | |
| 0 to 0.75 |
| Iron (Fe), % | 26.6 to 38.4 | |
| 77.8 to 85 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 3.5 to 5.0 | |
| 0 to 0.75 |
| Nickel (Ni), % | 35 to 40 | |
| 0 to 0.6 |
| Niobium (Nb), % | 0.15 to 0.35 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.9 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.030 |