N08135 Stainless Steel vs. ACI-ASTM CF3M Steel

Both N08135 stainless steel and ACI-ASTM CF3M steel are iron alloys. They have 70% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is ACI-ASTM CF3M steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
55
Fatigue Strength, MPa 220
270
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
78
Tensile Strength: Ultimate (UTS), MPa 570
520
Tensile Strength: Yield (Proof), MPa 240
260

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 430
420
Maximum Temperature: Mechanical, °C 1100
990
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1390
1430
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
15

Otherwise Unclassified Properties

Base Metal Price, % relative 39
19
Density, g/cm3 8.2
7.9
Embodied Carbon, kg CO2/kg material 6.8
3.8
Embodied Energy, MJ/kg 94
53
Embodied Water, L/kg 220
160

Common Calculations

PREN (Pitting Resistance) 38
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
240
Resilience: Unit (Modulus of Resilience), kJ/m3 140
170
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
18
Strength to Weight: Bending, points 19
18
Thermal Shock Resistance, points 13
12

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 20.5 to 23.5
17 to 21
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
59.9 to 72
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 4.0 to 5.0
2.0 to 3.0
Nickel (Ni), % 33 to 38
9.0 to 13
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.040
Tungsten (W), % 0.2 to 0.8
0