N08135 Stainless Steel vs. AISI 204 Stainless Steel

Both N08135 stainless steel and AISI 204 stainless steel are iron alloys. They have 55% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is AISI 204 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
23 to 39
Fatigue Strength, MPa 220
320 to 720
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Shear Strength, MPa 400
500 to 700
Tensile Strength: Ultimate (UTS), MPa 570
730 to 1100
Tensile Strength: Yield (Proof), MPa 240
380 to 1080

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 430
410
Maximum Temperature: Mechanical, °C 1100
850
Melting Completion (Liquidus), °C 1440
1410
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
17

Otherwise Unclassified Properties

Base Metal Price, % relative 39
10
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 6.8
2.4
Embodied Energy, MJ/kg 94
35
Embodied Water, L/kg 220
130

Common Calculations

PREN (Pitting Resistance) 38
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
240 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 140
360 to 2940
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
27 to 40
Strength to Weight: Bending, points 19
24 to 31
Thermal Shock Resistance, points 13
16 to 24

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 20.5 to 23.5
15 to 17
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
69.6 to 76.4
Manganese (Mn), % 0 to 1.0
7.0 to 9.0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 33 to 38
1.5 to 3.0
Nitrogen (N), % 0
0.15 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.2 to 0.8
0