N08135 Stainless Steel vs. AISI 304 Stainless Steel

Both N08135 stainless steel and AISI 304 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is AISI 304 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
8.0 to 43
Fatigue Strength, MPa 220
210 to 440
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Shear Strength, MPa 400
400 to 690
Tensile Strength: Ultimate (UTS), MPa 570
580 to 1180
Tensile Strength: Yield (Proof), MPa 240
230 to 860

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 430
420
Maximum Temperature: Mechanical, °C 1100
710
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
17

Otherwise Unclassified Properties

Base Metal Price, % relative 39
15
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 6.8
3.0
Embodied Energy, MJ/kg 94
43
Embodied Water, L/kg 220
150

Common Calculations

PREN (Pitting Resistance) 38
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
86 to 250
Resilience: Unit (Modulus of Resilience), kJ/m3 140
140 to 1870
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
21 to 42
Strength to Weight: Bending, points 19
20 to 32
Thermal Shock Resistance, points 13
12 to 25

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 20.5 to 23.5
18 to 20
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
66.5 to 74
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 33 to 38
8.0 to 10.5
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.75
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.2 to 0.8
0