N08135 Stainless Steel vs. AISI 310HCb Stainless Steel

Both N08135 stainless steel and AISI 310HCb stainless steel are iron alloys. They have 80% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is AISI 310HCb stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
46
Fatigue Strength, MPa 220
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
78
Shear Strength, MPa 400
410
Tensile Strength: Ultimate (UTS), MPa 570
590
Tensile Strength: Yield (Proof), MPa 240
230

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 430
520
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1440
1410
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
16

Otherwise Unclassified Properties

Base Metal Price, % relative 39
28
Density, g/cm3 8.2
7.9
Embodied Carbon, kg CO2/kg material 6.8
4.8
Embodied Energy, MJ/kg 94
69
Embodied Water, L/kg 220
190

Common Calculations

PREN (Pitting Resistance) 38
25
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
210
Resilience: Unit (Modulus of Resilience), kJ/m3 140
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
21
Strength to Weight: Bending, points 19
20
Thermal Shock Resistance, points 13
13

Alloy Composition

Carbon (C), % 0 to 0.030
0.040 to 0.1
Chromium (Cr), % 20.5 to 23.5
24 to 26
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
48 to 57
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 33 to 38
19 to 22
Niobium (Nb), % 0
0 to 1.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.75
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.2 to 0.8
0