N08135 Stainless Steel vs. ASTM A369 Grade FP91

Both N08135 stainless steel and ASTM A369 grade FP91 are iron alloys. They have 47% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is ASTM A369 grade FP91.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
19
Fatigue Strength, MPa 220
320
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
75
Shear Strength, MPa 400
410
Tensile Strength: Ultimate (UTS), MPa 570
670
Tensile Strength: Yield (Proof), MPa 240
460

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Maximum Temperature: Mechanical, °C 1100
600
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 39
7.0
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 6.8
2.6
Embodied Energy, MJ/kg 94
37
Embodied Water, L/kg 220
88

Common Calculations

PREN (Pitting Resistance) 38
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
560
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
24
Strength to Weight: Bending, points 19
22
Thermal Shock Resistance, points 13
18

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Carbon (C), % 0 to 0.030
0.080 to 0.12
Chromium (Cr), % 20.5 to 23.5
8.0 to 9.5
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
87.3 to 90.3
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 4.0 to 5.0
0.85 to 1.1
Nickel (Ni), % 33 to 38
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.75
0.2 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.025
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0.2 to 0.8
0
Vanadium (V), % 0
0.18 to 0.25
Zirconium (Zr), % 0
0 to 0.010