N08135 Stainless Steel vs. EN 1.0303 Steel

Both N08135 stainless steel and EN 1.0303 steel are iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.0303 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
12 to 25
Fatigue Strength, MPa 220
150 to 230
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
220 to 260
Tensile Strength: Ultimate (UTS), MPa 570
290 to 410
Tensile Strength: Yield (Proof), MPa 240
200 to 320

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1440
1470
Melting Onset (Solidus), °C 1390
1430
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 39
1.8
Density, g/cm3 8.2
7.9
Embodied Carbon, kg CO2/kg material 6.8
1.4
Embodied Energy, MJ/kg 94
18
Embodied Water, L/kg 220
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
30 to 94
Resilience: Unit (Modulus of Resilience), kJ/m3 140
110 to 270
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
10 to 15
Strength to Weight: Bending, points 19
12 to 16
Thermal Shock Resistance, points 13
9.2 to 13

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.060
Carbon (C), % 0 to 0.030
0.020 to 0.060
Chromium (Cr), % 20.5 to 23.5
0
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
99.335 to 99.71
Manganese (Mn), % 0 to 1.0
0.25 to 0.4
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 33 to 38
0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 0.75
0 to 0.1
Sulfur (S), % 0 to 0.030
0 to 0.025
Tungsten (W), % 0.2 to 0.8
0