N08135 Stainless Steel vs. EN 1.0644 Steel

Both N08135 stainless steel and EN 1.0644 steel are iron alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.0644 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
17
Fatigue Strength, MPa 220
380
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
420
Tensile Strength: Ultimate (UTS), MPa 570
690
Tensile Strength: Yield (Proof), MPa 240
570

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 39
2.4
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 6.8
1.8
Embodied Energy, MJ/kg 94
24
Embodied Water, L/kg 220
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
870
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
24
Strength to Weight: Bending, points 19
22
Thermal Shock Resistance, points 13
22

Alloy Composition

Aluminum (Al), % 0
0.010 to 0.050
Carbon (C), % 0 to 0.030
0.16 to 0.22
Chromium (Cr), % 20.5 to 23.5
0 to 0.3
Copper (Cu), % 0 to 0.7
0 to 0.3
Iron (Fe), % 30.2 to 42.3
96.1 to 98.4
Manganese (Mn), % 0 to 1.0
1.3 to 1.7
Molybdenum (Mo), % 4.0 to 5.0
0 to 0.080
Nickel (Ni), % 33 to 38
0 to 0.4
Niobium (Nb), % 0
0 to 0.070
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.75
0.1 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.035
Titanium (Ti), % 0
0 to 0.050
Tungsten (W), % 0.2 to 0.8
0
Vanadium (V), % 0
0.080 to 0.15