MakeItFrom.com
Menu (ESC)

N08135 Stainless Steel vs. EN 1.4105 Stainless Steel

Both N08135 stainless steel and EN 1.4105 stainless steel are iron alloys. They have 55% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.4105 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
23
Fatigue Strength, MPa 220
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Shear Strength, MPa 400
340
Tensile Strength: Ultimate (UTS), MPa 570
530
Tensile Strength: Yield (Proof), MPa 240
290

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 430
410
Maximum Temperature: Mechanical, °C 1100
870
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
10

Otherwise Unclassified Properties

Base Metal Price, % relative 39
9.0
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 6.8
2.2
Embodied Energy, MJ/kg 94
31
Embodied Water, L/kg 220
120

Common Calculations

PREN (Pitting Resistance) 38
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
100
Resilience: Unit (Modulus of Resilience), kJ/m3 140
210
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
19
Strength to Weight: Bending, points 19
19
Thermal Shock Resistance, points 13
19

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 20.5 to 23.5
16 to 18
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
77.9 to 83.7
Manganese (Mn), % 0 to 1.0
0 to 1.5
Molybdenum (Mo), % 4.0 to 5.0
0.2 to 0.6
Nickel (Ni), % 33 to 38
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.5
Sulfur (S), % 0 to 0.030
0.15 to 0.35
Tungsten (W), % 0.2 to 0.8
0