N08135 Stainless Steel vs. EN 1.4113 Stainless Steel

Both N08135 stainless steel and EN 1.4113 stainless steel are iron alloys. They have 55% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.4113 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
20
Fatigue Strength, MPa 220
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
78
Shear Strength, MPa 400
340
Tensile Strength: Ultimate (UTS), MPa 570
540
Tensile Strength: Yield (Proof), MPa 240
310

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 430
410
Maximum Temperature: Mechanical, °C 1100
880
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
10

Otherwise Unclassified Properties

Base Metal Price, % relative 39
9.5
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 6.8
2.4
Embodied Energy, MJ/kg 94
33
Embodied Water, L/kg 220
120

Common Calculations

PREN (Pitting Resistance) 38
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
94
Resilience: Unit (Modulus of Resilience), kJ/m3 140
240
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
19
Strength to Weight: Bending, points 19
19
Thermal Shock Resistance, points 13
20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 20.5 to 23.5
16 to 18
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
78.5 to 83.1
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 4.0 to 5.0
0.9 to 1.4
Nickel (Ni), % 33 to 38
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 0.2 to 0.8
0