N08135 Stainless Steel vs. EN 1.4125 Stainless Steel

Both N08135 stainless steel and EN 1.4125 stainless steel are iron alloys. They have 55% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.4125 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
19
Fatigue Strength, MPa 220
300
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Shear Strength, MPa 400
500
Tensile Strength: Ultimate (UTS), MPa 570
800
Tensile Strength: Yield (Proof), MPa 240
470

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 430
390
Maximum Temperature: Mechanical, °C 1100
870
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
10

Otherwise Unclassified Properties

Base Metal Price, % relative 39
9.0
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 6.8
2.3
Embodied Energy, MJ/kg 94
32
Embodied Water, L/kg 220
120

Common Calculations

PREN (Pitting Resistance) 38
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
130
Resilience: Unit (Modulus of Resilience), kJ/m3 140
570
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
29
Strength to Weight: Bending, points 19
25
Thermal Shock Resistance, points 13
29

Alloy Composition

Carbon (C), % 0 to 0.030
1.0 to 1.2
Chromium (Cr), % 20.5 to 23.5
16 to 18
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
78 to 82.7
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 4.0 to 5.0
0.4 to 0.8
Nickel (Ni), % 33 to 38
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 0.2 to 0.8
0