MakeItFrom.com
Menu (ESC)

N08135 Stainless Steel vs. EN 1.4474 Stainless Steel

Both N08135 stainless steel and EN 1.4474 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 66% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.4474 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
23
Fatigue Strength, MPa 220
320
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 80
80
Tensile Strength: Ultimate (UTS), MPa 570
670
Tensile Strength: Yield (Proof), MPa 240
480

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Maximum Temperature: Corrosion, °C 430
450
Maximum Temperature: Mechanical, °C 1100
1100
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 39
17
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 6.8
3.4
Embodied Energy, MJ/kg 94
48
Embodied Water, L/kg 220
170

Common Calculations

PREN (Pitting Resistance) 38
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
140
Resilience: Unit (Modulus of Resilience), kJ/m3 140
560
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
24
Strength to Weight: Bending, points 19
22
Thermal Shock Resistance, points 13
18

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 20.5 to 23.5
25 to 27
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
61.2 to 69.1
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
1.3 to 2.0
Nickel (Ni), % 33 to 38
4.5 to 6.5
Nitrogen (N), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.025
Tungsten (W), % 0.2 to 0.8
0