N08135 Stainless Steel vs. EN 1.4634 Stainless Steel

Both N08135 stainless steel and EN 1.4634 stainless steel are iron alloys. They have 56% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.4634 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
21
Fatigue Strength, MPa 220
180
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
77
Shear Strength, MPa 400
340
Tensile Strength: Ultimate (UTS), MPa 570
540
Tensile Strength: Yield (Proof), MPa 240
280

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 430
500
Maximum Temperature: Mechanical, °C 1100
900
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
10

Otherwise Unclassified Properties

Base Metal Price, % relative 39
13
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 6.8
2.9
Embodied Energy, MJ/kg 94
42
Embodied Water, L/kg 220
140

Common Calculations

PREN (Pitting Resistance) 38
19
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
93
Resilience: Unit (Modulus of Resilience), kJ/m3 140
200
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
20
Strength to Weight: Bending, points 19
19
Thermal Shock Resistance, points 13
19

Alloy Composition

Aluminum (Al), % 0
0.2 to 1.5
Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 20.5 to 23.5
17.5 to 18.5
Copper (Cu), % 0 to 0.7
0 to 0.5
Iron (Fe), % 30.2 to 42.3
74.9 to 81.8
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 4.0 to 5.0
0 to 0.5
Nickel (Ni), % 33 to 38
0 to 0.5
Niobium (Nb), % 0
0.3 to 1.0
Phosphorus (P), % 0 to 0.030
0 to 0.050
Silicon (Si), % 0 to 0.75
0.2 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.050
Tungsten (W), % 0.2 to 0.8
0