MakeItFrom.com
Menu (ESC)

N08135 Stainless Steel vs. EN 1.4662 Stainless Steel

Both N08135 stainless steel and EN 1.4662 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.4662 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
28
Fatigue Strength, MPa 220
430 to 450
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 80
79
Shear Strength, MPa 400
520 to 540
Tensile Strength: Ultimate (UTS), MPa 570
810 to 830
Tensile Strength: Yield (Proof), MPa 240
580 to 620

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 430
440
Maximum Temperature: Mechanical, °C 1100
1090
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 39
16
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 6.8
3.2
Embodied Energy, MJ/kg 94
45
Embodied Water, L/kg 220
170

Common Calculations

PREN (Pitting Resistance) 38
33
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
210
Resilience: Unit (Modulus of Resilience), kJ/m3 140
840 to 940
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
29 to 30
Strength to Weight: Bending, points 19
25
Thermal Shock Resistance, points 13
22

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 20.5 to 23.5
23 to 25
Copper (Cu), % 0 to 0.7
0.1 to 0.8
Iron (Fe), % 30.2 to 42.3
62.6 to 70.2
Manganese (Mn), % 0 to 1.0
2.5 to 4.0
Molybdenum (Mo), % 4.0 to 5.0
1.0 to 2.0
Nickel (Ni), % 33 to 38
3.0 to 4.5
Nitrogen (N), % 0
0.2 to 0.3
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.75
0 to 0.7
Sulfur (S), % 0 to 0.030
0 to 0.0050
Tungsten (W), % 0.2 to 0.8
0