N08135 Stainless Steel vs. EN 1.4865 Stainless Steel

Both N08135 stainless steel and EN 1.4865 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.4865 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
6.8
Fatigue Strength, MPa 220
120
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 570
470
Tensile Strength: Yield (Proof), MPa 240
250

Thermal Properties

Latent Heat of Fusion, J/g 310
320
Maximum Temperature: Corrosion, °C 430
410
Maximum Temperature: Mechanical, °C 1100
1020
Melting Completion (Liquidus), °C 1440
1380
Melting Onset (Solidus), °C 1390
1330
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
15

Otherwise Unclassified Properties

Base Metal Price, % relative 39
33
Density, g/cm3 8.2
8.0
Embodied Carbon, kg CO2/kg material 6.8
5.8
Embodied Energy, MJ/kg 94
81
Embodied Water, L/kg 220
200

Common Calculations

PREN (Pitting Resistance) 38
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
27
Resilience: Unit (Modulus of Resilience), kJ/m3 140
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
16
Strength to Weight: Bending, points 19
17
Thermal Shock Resistance, points 13
11

Alloy Composition

Carbon (C), % 0 to 0.030
0.3 to 0.5
Chromium (Cr), % 20.5 to 23.5
18 to 21
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
34.4 to 44.7
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
0 to 0.5
Nickel (Ni), % 33 to 38
36 to 39
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.75
1.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.2 to 0.8
0