N08135 Stainless Steel vs. EN 1.5510 Steel

Both N08135 stainless steel and EN 1.5510 steel are iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.5510 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
11 to 21
Fatigue Strength, MPa 220
220 to 330
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
310 to 380
Tensile Strength: Ultimate (UTS), MPa 570
450 to 1600
Tensile Strength: Yield (Proof), MPa 240
310 to 520

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 39
1.9
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 6.8
1.4
Embodied Energy, MJ/kg 94
19
Embodied Water, L/kg 220
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
46 to 260
Resilience: Unit (Modulus of Resilience), kJ/m3 140
260 to 710
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
16 to 57
Strength to Weight: Bending, points 19
17 to 39
Thermal Shock Resistance, points 13
13 to 47

Alloy Composition

Boron (B), % 0
0.00080 to 0.0050
Carbon (C), % 0 to 0.030
0.25 to 0.3
Chromium (Cr), % 20.5 to 23.5
0 to 0.3
Copper (Cu), % 0 to 0.7
0 to 0.25
Iron (Fe), % 30.2 to 42.3
97.9 to 99.149
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 33 to 38
0
Phosphorus (P), % 0 to 0.030
0 to 0.025
Silicon (Si), % 0 to 0.75
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025
Tungsten (W), % 0.2 to 0.8
0