N08135 Stainless Steel vs. EN 1.7216 Steel

Both N08135 stainless steel and EN 1.7216 steel are iron alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.7216 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
12 to 23
Fatigue Strength, MPa 220
290 to 440
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
410 to 560
Tensile Strength: Ultimate (UTS), MPa 570
650 to 930
Tensile Strength: Yield (Proof), MPa 240
400 to 690

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
420
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 39
2.4
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 6.8
1.5
Embodied Energy, MJ/kg 94
20
Embodied Water, L/kg 220
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
110 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 140
430 to 1280
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
23 to 33
Strength to Weight: Bending, points 19
21 to 27
Thermal Shock Resistance, points 13
19 to 27

Alloy Composition

Carbon (C), % 0 to 0.030
0.27 to 0.34
Chromium (Cr), % 20.5 to 23.5
0.8 to 1.2
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
97.2 to 98.4
Manganese (Mn), % 0 to 1.0
0.35 to 0.6
Molybdenum (Mo), % 4.0 to 5.0
0.15 to 0.3
Nickel (Ni), % 33 to 38
0
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.75
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.035
Tungsten (W), % 0.2 to 0.8
0