N08135 Stainless Steel vs. EN 1.8833 Steel

Both N08135 stainless steel and EN 1.8833 steel are iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is EN 1.8833 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
25
Fatigue Strength, MPa 220
280
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
340
Tensile Strength: Ultimate (UTS), MPa 570
530
Tensile Strength: Yield (Proof), MPa 240
390

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 39
2.3
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 6.8
1.6
Embodied Energy, MJ/kg 94
21
Embodied Water, L/kg 220
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
400
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
19
Strength to Weight: Bending, points 19
19
Thermal Shock Resistance, points 13
16

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.030
Carbon (C), % 0 to 0.030
0 to 0.14
Chromium (Cr), % 20.5 to 23.5
0
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
96.8 to 99.98
Manganese (Mn), % 0 to 1.0
0 to 1.6
Molybdenum (Mo), % 4.0 to 5.0
0 to 0.2
Nickel (Ni), % 33 to 38
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 0.75
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.0050
Titanium (Ti), % 0
0 to 0.050
Tungsten (W), % 0.2 to 0.8
0
Vanadium (V), % 0
0 to 0.1