N08135 Stainless Steel vs. SAE-AISI 1330 Steel

Both N08135 stainless steel and SAE-AISI 1330 steel are iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is SAE-AISI 1330 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
11 to 23
Fatigue Strength, MPa 220
210 to 380
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
330 to 430
Tensile Strength: Ultimate (UTS), MPa 570
520 to 710
Tensile Strength: Yield (Proof), MPa 240
290 to 610

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 39
1.9
Density, g/cm3 8.2
7.8
Embodied Carbon, kg CO2/kg material 6.8
1.4
Embodied Energy, MJ/kg 94
19
Embodied Water, L/kg 220
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
76 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 140
230 to 990
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
19 to 25
Strength to Weight: Bending, points 19
18 to 23
Thermal Shock Resistance, points 13
17 to 23

Alloy Composition

Carbon (C), % 0 to 0.030
0.28 to 0.33
Chromium (Cr), % 20.5 to 23.5
0
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
97.3 to 98
Manganese (Mn), % 0 to 1.0
1.6 to 1.9
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 33 to 38
0
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.75
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040
Tungsten (W), % 0.2 to 0.8
0