N08135 Stainless Steel vs. SAE-AISI 4815 Steel

Both N08135 stainless steel and SAE-AISI 4815 steel are iron alloys. They have 41% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is SAE-AISI 4815 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
23
Fatigue Strength, MPa 220
260
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 400
350
Tensile Strength: Ultimate (UTS), MPa 570
550
Tensile Strength: Yield (Proof), MPa 240
370

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1100
410
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 39
4.3
Density, g/cm3 8.2
7.9
Embodied Carbon, kg CO2/kg material 6.8
1.8
Embodied Energy, MJ/kg 94
24
Embodied Water, L/kg 220
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
110
Resilience: Unit (Modulus of Resilience), kJ/m3 140
360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
20
Strength to Weight: Bending, points 19
19
Thermal Shock Resistance, points 13
18

Alloy Composition

Carbon (C), % 0 to 0.030
0.13 to 0.18
Chromium (Cr), % 20.5 to 23.5
0
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
94.7 to 95.9
Manganese (Mn), % 0 to 1.0
0.4 to 0.6
Molybdenum (Mo), % 4.0 to 5.0
0.2 to 0.3
Nickel (Ni), % 33 to 38
3.3 to 3.8
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.75
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040
Tungsten (W), % 0.2 to 0.8
0