N08135 Stainless Steel vs. SAE-AISI 9255 Steel

Both N08135 stainless steel and SAE-AISI 9255 steel are iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is SAE-AISI 9255 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 46
21
Fatigue Strength, MPa 220
270
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
72
Shear Strength, MPa 400
430
Tensile Strength: Ultimate (UTS), MPa 570
680
Tensile Strength: Yield (Proof), MPa 240
390

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 39
2.0
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 6.8
1.5
Embodied Energy, MJ/kg 94
20
Embodied Water, L/kg 220
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
400
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
24
Strength to Weight: Bending, points 19
22
Thermal Shock Resistance, points 13
21

Alloy Composition

Carbon (C), % 0 to 0.030
0.51 to 0.59
Chromium (Cr), % 20.5 to 23.5
0
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
96.2 to 97
Manganese (Mn), % 0 to 1.0
0.7 to 1.0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 33 to 38
0
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0 to 0.75
1.8 to 2.2
Sulfur (S), % 0 to 0.030
0 to 0.040
Tungsten (W), % 0.2 to 0.8
0