N08135 Stainless Steel vs. SAE-AISI F1 Steel

Both N08135 stainless steel and SAE-AISI F1 steel are iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is SAE-AISI F1 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
72
Tensile Strength: Ultimate (UTS), MPa 570
620 to 2320

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1440
1480
Melting Onset (Solidus), °C 1390
1430
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 39
5.0
Density, g/cm3 8.2
7.9
Embodied Carbon, kg CO2/kg material 6.8
1.7
Embodied Energy, MJ/kg 94
24
Embodied Water, L/kg 220
46

Common Calculations

PREN (Pitting Resistance) 38
2.3
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
22 to 82
Strength to Weight: Bending, points 19
20 to 49
Thermal Shock Resistance, points 13
19 to 70

Alloy Composition

Carbon (C), % 0 to 0.030
1.0 to 1.3
Chromium (Cr), % 20.5 to 23.5
0
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
95.9 to 98
Manganese (Mn), % 0 to 1.0
0 to 0.5
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 33 to 38
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.75
0.1 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.2 to 0.8
1.0 to 1.8