N08135 Stainless Steel vs. R30816 Cobalt

N08135 stainless steel belongs to the iron alloys classification, while R30816 cobalt belongs to the cobalt alloys. They have 48% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is R30816 cobalt.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 46
23
Fatigue Strength, MPa 220
250
Poisson's Ratio 0.28
0.3
Shear Modulus, GPa 80
81
Tensile Strength: Ultimate (UTS), MPa 570
1020
Tensile Strength: Yield (Proof), MPa 240
460

Thermal Properties

Latent Heat of Fusion, J/g 310
300
Melting Completion (Liquidus), °C 1440
1540
Melting Onset (Solidus), °C 1390
1460
Specific Heat Capacity, J/kg-K 460
420
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Density, g/cm3 8.2
9.1
Embodied Carbon, kg CO2/kg material 6.8
20
Embodied Energy, MJ/kg 94
320
Embodied Water, L/kg 220
440

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
190
Resilience: Unit (Modulus of Resilience), kJ/m3 140
510
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 19
31
Strength to Weight: Bending, points 19
25
Thermal Shock Resistance, points 13
28

Alloy Composition

Carbon (C), % 0 to 0.030
0.32 to 0.42
Chromium (Cr), % 20.5 to 23.5
19 to 21
Cobalt (Co), % 0
40 to 49.8
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
0 to 5.0
Manganese (Mn), % 0 to 1.0
1.0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
3.5 to 4.5
Nickel (Ni), % 33 to 38
19 to 21
Niobium (Nb), % 0
3.5 to 4.5
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tantalum (Ta), % 0
3.5 to 4.5
Tungsten (W), % 0.2 to 0.8
3.5 to 4.5