N08135 Stainless Steel vs. S21600 Stainless Steel

Both N08135 stainless steel and S21600 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is S21600 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
46
Fatigue Strength, MPa 220
360
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
79
Shear Strength, MPa 400
500
Tensile Strength: Ultimate (UTS), MPa 570
710
Tensile Strength: Yield (Proof), MPa 240
390

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 430
420
Maximum Temperature: Mechanical, °C 1100
990
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1390
1380
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
17

Otherwise Unclassified Properties

Base Metal Price, % relative 39
17
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 6.8
3.6
Embodied Energy, MJ/kg 94
50
Embodied Water, L/kg 220
160

Common Calculations

PREN (Pitting Resistance) 38
34
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
270
Resilience: Unit (Modulus of Resilience), kJ/m3 140
370
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
25
Strength to Weight: Bending, points 19
23
Thermal Shock Resistance, points 13
15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 20.5 to 23.5
17.5 to 22
Copper (Cu), % 0 to 0.7
0
Iron (Fe), % 30.2 to 42.3
57.6 to 67.8
Manganese (Mn), % 0 to 1.0
7.5 to 9.0
Molybdenum (Mo), % 4.0 to 5.0
2.0 to 3.0
Nickel (Ni), % 33 to 38
5.0 to 7.0
Nitrogen (N), % 0
0.25 to 0.5
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.75
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.2 to 0.8
0