N08135 Stainless Steel vs. S32101 Stainless Steel

Both N08135 stainless steel and S32101 stainless steel are iron alloys. They have 61% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08135 stainless steel and the bottom bar is S32101 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 46
34
Fatigue Strength, MPa 220
400
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
78
Shear Strength, MPa 400
490
Tensile Strength: Ultimate (UTS), MPa 570
740
Tensile Strength: Yield (Proof), MPa 240
500

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 430
430
Maximum Temperature: Mechanical, °C 1100
1000
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 460
480
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 39
12
Density, g/cm3 8.2
7.7
Embodied Carbon, kg CO2/kg material 6.8
2.6
Embodied Energy, MJ/kg 94
38
Embodied Water, L/kg 220
150

Common Calculations

PREN (Pitting Resistance) 38
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
230
Resilience: Unit (Modulus of Resilience), kJ/m3 140
640
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
27
Strength to Weight: Bending, points 19
24
Thermal Shock Resistance, points 13
20

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.040
Chromium (Cr), % 20.5 to 23.5
21 to 22
Copper (Cu), % 0 to 0.7
0.1 to 0.8
Iron (Fe), % 30.2 to 42.3
67.3 to 73.3
Manganese (Mn), % 0 to 1.0
4.0 to 6.0
Molybdenum (Mo), % 4.0 to 5.0
0.1 to 0.8
Nickel (Ni), % 33 to 38
1.4 to 1.7
Nitrogen (N), % 0
0.2 to 0.25
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tungsten (W), % 0.2 to 0.8
0