N08330 Stainless Steel vs. AWS ENiCrCoMo-1

N08330 stainless steel belongs to the iron alloys classification, while AWS ENiCrCoMo-1 belongs to the nickel alloys. They have 58% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is AWS ENiCrCoMo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 34
28
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
82
Tensile Strength: Ultimate (UTS), MPa 550
710

Thermal Properties

Latent Heat of Fusion, J/g 310
330
Melting Completion (Liquidus), °C 1390
1430
Melting Onset (Solidus), °C 1340
1380
Specific Heat Capacity, J/kg-K 480
440
Thermal Expansion, µm/m-K 16
13

Otherwise Unclassified Properties

Base Metal Price, % relative 32
75
Density, g/cm3 8.0
8.5
Embodied Carbon, kg CO2/kg material 5.4
11
Embodied Energy, MJ/kg 77
140
Embodied Water, L/kg 190
340

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 19
23
Strength to Weight: Bending, points 18
21
Thermal Shock Resistance, points 13
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.080
0.050 to 0.15
Chromium (Cr), % 17 to 20
21 to 26
Cobalt (Co), % 0
9.0 to 15
Copper (Cu), % 0 to 1.0
0 to 0.5
Iron (Fe), % 38.3 to 48.3
0 to 5.0
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0.3 to 2.5
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 34 to 37
38.6 to 61.7
Niobium (Nb), % 0
0 to 1.0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0.75 to 1.5
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.015
Tin (Sn), % 0 to 0.025
0
Residuals, % 0
0 to 0.5