N08330 Stainless Steel vs. EN 1.4057 Stainless Steel

Both N08330 stainless steel and EN 1.4057 stainless steel are iron alloys. They have 63% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is EN 1.4057 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
11 to 17
Fatigue Strength, MPa 190
320 to 430
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Shear Strength, MPa 360
520 to 580
Tensile Strength: Ultimate (UTS), MPa 550
840 to 980
Tensile Strength: Yield (Proof), MPa 230
530 to 790

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Maximum Temperature: Corrosion, °C 420
400
Maximum Temperature: Mechanical, °C 1050
850
Melting Completion (Liquidus), °C 1390
1440
Melting Onset (Solidus), °C 1340
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 12
25
Thermal Expansion, µm/m-K 16
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 32
9.5
Density, g/cm3 8.0
7.7
Embodied Carbon, kg CO2/kg material 5.4
2.2
Embodied Energy, MJ/kg 77
32
Embodied Water, L/kg 190
120

Common Calculations

PREN (Pitting Resistance) 19
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
96 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 140
700 to 1610
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
30 to 35
Strength to Weight: Bending, points 18
26 to 28
Thermal Diffusivity, mm2/s 3.1
6.7
Thermal Shock Resistance, points 13
30 to 35

Alloy Composition

Carbon (C), % 0 to 0.080
0.12 to 0.22
Chromium (Cr), % 17 to 20
15 to 17
Copper (Cu), % 0 to 1.0
0
Iron (Fe), % 38.3 to 48.3
77.7 to 83.4
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0 to 1.5
Nickel (Ni), % 34 to 37
1.5 to 2.5
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0.75 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Tin (Sn), % 0 to 0.025
0