N08330 Stainless Steel vs. EN 1.5663 Steel

Both N08330 stainless steel and EN 1.5663 steel are iron alloys. They have 53% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is EN 1.5663 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
230
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
20
Fatigue Strength, MPa 190
450
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 360
470
Tensile Strength: Ultimate (UTS), MPa 550
750
Tensile Strength: Yield (Proof), MPa 230
660

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1050
430
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
8.7
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
9.8

Otherwise Unclassified Properties

Base Metal Price, % relative 32
7.5
Density, g/cm3 8.0
8.0
Embodied Carbon, kg CO2/kg material 5.4
2.3
Embodied Energy, MJ/kg 77
31
Embodied Water, L/kg 190
63

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
150
Resilience: Unit (Modulus of Resilience), kJ/m3 140
1150
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
26
Strength to Weight: Bending, points 18
23
Thermal Shock Resistance, points 13
22

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.1
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0 to 1.0
0
Iron (Fe), % 38.3 to 48.3
88.6 to 91.2
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0.3 to 0.8
Molybdenum (Mo), % 0
0 to 0.1
Nickel (Ni), % 34 to 37
8.5 to 10
Phosphorus (P), % 0 to 0.030
0 to 0.015
Silicon (Si), % 0.75 to 1.5
0 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.0050
Tin (Sn), % 0 to 0.025
0
Vanadium (V), % 0
0 to 0.010