N08330 Stainless Steel vs. EN 1.8967 Steel

Both N08330 stainless steel and EN 1.8967 steel are iron alloys. They have 46% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is EN 1.8967 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
170
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
16
Fatigue Strength, MPa 190
220
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Shear Strength, MPa 360
350
Tensile Strength: Ultimate (UTS), MPa 550
570
Tensile Strength: Yield (Proof), MPa 230
340

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1050
420
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 12
39
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 32
3.0
Density, g/cm3 8.0
7.8
Embodied Carbon, kg CO2/kg material 5.4
1.8
Embodied Energy, MJ/kg 77
25
Embodied Water, L/kg 190
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
78
Resilience: Unit (Modulus of Resilience), kJ/m3 140
300
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
20
Strength to Weight: Bending, points 18
19
Thermal Diffusivity, mm2/s 3.1
10
Thermal Shock Resistance, points 13
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.030
Carbon (C), % 0 to 0.080
0 to 0.19
Chromium (Cr), % 17 to 20
0.35 to 0.85
Copper (Cu), % 0 to 1.0
0.2 to 0.6
Iron (Fe), % 38.3 to 48.3
94.6 to 99
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0.45 to 1.6
Molybdenum (Mo), % 0
0 to 0.35
Nickel (Ni), % 34 to 37
0 to 0.7
Niobium (Nb), % 0
0 to 0.065
Phosphorus (P), % 0 to 0.030
0 to 0.035
Silicon (Si), % 0.75 to 1.5
0 to 0.55
Sulfur (S), % 0 to 0.030
0 to 0.035
Tin (Sn), % 0 to 0.025
0
Titanium (Ti), % 0
0 to 0.12
Vanadium (V), % 0
0 to 0.14
Zirconium (Zr), % 0
0 to 0.17