N08330 Stainless Steel vs. CC482K Bronze

N08330 stainless steel belongs to the iron alloys classification, while CC482K bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is CC482K bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
99
Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
5.6
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
40
Tensile Strength: Ultimate (UTS), MPa 550
300
Tensile Strength: Yield (Proof), MPa 230
160

Thermal Properties

Latent Heat of Fusion, J/g 310
190
Maximum Temperature: Mechanical, °C 1050
160
Melting Completion (Liquidus), °C 1390
980
Melting Onset (Solidus), °C 1340
860
Specific Heat Capacity, J/kg-K 480
360
Thermal Conductivity, W/m-K 12
64
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
10
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
10

Otherwise Unclassified Properties

Base Metal Price, % relative 32
36
Density, g/cm3 8.0
8.8
Embodied Carbon, kg CO2/kg material 5.4
3.8
Embodied Energy, MJ/kg 77
62
Embodied Water, L/kg 190
400

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
14
Resilience: Unit (Modulus of Resilience), kJ/m3 140
120
Stiffness to Weight: Axial, points 14
6.8
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 19
9.5
Strength to Weight: Bending, points 18
11
Thermal Diffusivity, mm2/s 3.1
20
Thermal Shock Resistance, points 13
11

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.2
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0 to 1.0
83.5 to 87
Iron (Fe), % 38.3 to 48.3
0 to 0.2
Lead (Pb), % 0 to 0.0050
0.7 to 2.5
Manganese (Mn), % 0 to 2.0
0 to 0.2
Nickel (Ni), % 34 to 37
0 to 2.0
Phosphorus (P), % 0 to 0.030
0 to 0.4
Silicon (Si), % 0.75 to 1.5
0 to 0.010
Sulfur (S), % 0 to 0.030
0 to 0.080
Tin (Sn), % 0 to 0.025
10.5 to 12.5
Zinc (Zn), % 0
0 to 2.0