N08330 Stainless Steel vs. Grade CW6MC Nickel

N08330 stainless steel belongs to the iron alloys classification, while grade CW6MC nickel belongs to the nickel alloys. They have 58% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is grade CW6MC nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
28
Fatigue Strength, MPa 190
210
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
79
Tensile Strength: Ultimate (UTS), MPa 550
540
Tensile Strength: Yield (Proof), MPa 230
310

Thermal Properties

Latent Heat of Fusion, J/g 310
330
Maximum Temperature: Mechanical, °C 1050
980
Melting Completion (Liquidus), °C 1390
1480
Melting Onset (Solidus), °C 1340
1430
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 12
11
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
1.3
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
1.4

Otherwise Unclassified Properties

Base Metal Price, % relative 32
80
Density, g/cm3 8.0
8.6
Embodied Carbon, kg CO2/kg material 5.4
14
Embodied Energy, MJ/kg 77
200
Embodied Water, L/kg 190
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
130
Resilience: Unit (Modulus of Resilience), kJ/m3 140
240
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 19
18
Strength to Weight: Bending, points 18
17
Thermal Diffusivity, mm2/s 3.1
2.8
Thermal Shock Resistance, points 13
15

Alloy Composition

Carbon (C), % 0 to 0.080
0 to 0.060
Chromium (Cr), % 17 to 20
20 to 23
Copper (Cu), % 0 to 1.0
0
Iron (Fe), % 38.3 to 48.3
0 to 5.0
Lead (Pb), % 0 to 0.0050
0
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 34 to 37
55.4 to 68.9
Niobium (Nb), % 0
3.2 to 4.5
Phosphorus (P), % 0 to 0.030
0 to 0.015
Silicon (Si), % 0.75 to 1.5
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Tin (Sn), % 0 to 0.025
0