N08330 Stainless Steel vs. C27000 Brass

N08330 stainless steel belongs to the iron alloys classification, while C27000 brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is C27000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Poisson's Ratio 0.28
0.31
Rockwell B Hardness 80
53 to 91
Shear Modulus, GPa 76
40
Tensile Strength: Ultimate (UTS), MPa 550
370 to 650

Thermal Properties

Latent Heat of Fusion, J/g 310
180
Maximum Temperature: Mechanical, °C 1050
130
Melting Completion (Liquidus), °C 1390
930
Melting Onset (Solidus), °C 1340
900
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 12
120
Thermal Expansion, µm/m-K 16
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
27
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
30

Otherwise Unclassified Properties

Base Metal Price, % relative 32
24
Density, g/cm3 8.0
8.1
Embodied Carbon, kg CO2/kg material 5.4
2.7
Embodied Energy, MJ/kg 77
45
Embodied Water, L/kg 190
320

Common Calculations

Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 19
13 to 22
Strength to Weight: Bending, points 18
14 to 21
Thermal Diffusivity, mm2/s 3.1
37
Thermal Shock Resistance, points 13
12 to 22

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0 to 1.0
63 to 68.5
Iron (Fe), % 38.3 to 48.3
0 to 0.1
Lead (Pb), % 0 to 0.0050
0 to 0.070
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 34 to 37
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.75 to 1.5
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0 to 0.025
0
Zinc (Zn), % 0
31 to 37
Residuals, % 0
0 to 0.3