N08330 Stainless Steel vs. C51000 Bronze

N08330 stainless steel belongs to the iron alloys classification, while C51000 bronze belongs to the copper alloys. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is C51000 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
2.7 to 64
Poisson's Ratio 0.28
0.34
Rockwell B Hardness 80
26 to 97
Shear Modulus, GPa 76
42
Shear Strength, MPa 360
250 to 460
Tensile Strength: Ultimate (UTS), MPa 550
330 to 780
Tensile Strength: Yield (Proof), MPa 230
130 to 750

Thermal Properties

Latent Heat of Fusion, J/g 310
200
Maximum Temperature: Mechanical, °C 1050
190
Melting Completion (Liquidus), °C 1390
1050
Melting Onset (Solidus), °C 1340
960
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 12
77
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
18
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
18

Otherwise Unclassified Properties

Base Metal Price, % relative 32
33
Density, g/cm3 8.0
8.8
Embodied Carbon, kg CO2/kg material 5.4
3.1
Embodied Energy, MJ/kg 77
50
Embodied Water, L/kg 190
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
7.0 to 490
Resilience: Unit (Modulus of Resilience), kJ/m3 140
75 to 2490
Stiffness to Weight: Axial, points 14
7.0
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 19
10 to 25
Strength to Weight: Bending, points 18
12 to 21
Thermal Diffusivity, mm2/s 3.1
23
Thermal Shock Resistance, points 13
12 to 28

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0 to 1.0
92.9 to 95.5
Iron (Fe), % 38.3 to 48.3
0 to 0.1
Lead (Pb), % 0 to 0.0050
0 to 0.050
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 34 to 37
0
Phosphorus (P), % 0 to 0.030
0.030 to 0.35
Silicon (Si), % 0.75 to 1.5
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0 to 0.025
4.5 to 5.8
Zinc (Zn), % 0
0 to 0.3
Residuals, % 0
0 to 0.5