N08330 Stainless Steel vs. C63200 Bronze

N08330 stainless steel belongs to the iron alloys classification, while C63200 bronze belongs to the copper alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is C63200 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 34
17 to 18
Poisson's Ratio 0.28
0.34
Rockwell B Hardness 80
88
Shear Modulus, GPa 76
44
Shear Strength, MPa 360
390 to 440
Tensile Strength: Ultimate (UTS), MPa 550
640 to 710
Tensile Strength: Yield (Proof), MPa 230
310 to 350

Thermal Properties

Latent Heat of Fusion, J/g 310
230
Maximum Temperature: Mechanical, °C 1050
230
Melting Completion (Liquidus), °C 1390
1060
Melting Onset (Solidus), °C 1340
1040
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 12
35
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
7.6

Otherwise Unclassified Properties

Base Metal Price, % relative 32
29
Density, g/cm3 8.0
8.3
Embodied Carbon, kg CO2/kg material 5.4
3.4
Embodied Energy, MJ/kg 77
55
Embodied Water, L/kg 190
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
95 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 140
400 to 510
Stiffness to Weight: Axial, points 14
7.9
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 19
21 to 24
Strength to Weight: Bending, points 18
20 to 21
Thermal Diffusivity, mm2/s 3.1
9.6
Thermal Shock Resistance, points 13
22 to 24

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
8.7 to 9.5
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0 to 1.0
78.8 to 82.6
Iron (Fe), % 38.3 to 48.3
3.5 to 4.3
Lead (Pb), % 0 to 0.0050
0 to 0.020
Manganese (Mn), % 0 to 2.0
1.2 to 2.0
Nickel (Ni), % 34 to 37
4.0 to 4.8
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.75 to 1.5
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0 to 0.025
0
Residuals, % 0
0 to 0.5