N08330 Stainless Steel vs. C63800 Bronze

N08330 stainless steel belongs to the iron alloys classification, while C63800 bronze belongs to the copper alloys. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is C63800 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
7.9 to 41
Poisson's Ratio 0.28
0.34
Rockwell B Hardness 80
94 to 110
Shear Modulus, GPa 76
43
Shear Strength, MPa 360
320 to 500
Tensile Strength: Ultimate (UTS), MPa 550
460 to 1010

Thermal Properties

Latent Heat of Fusion, J/g 310
240
Maximum Temperature: Mechanical, °C 1050
200
Melting Completion (Liquidus), °C 1390
1030
Melting Onset (Solidus), °C 1340
1000
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 12
40
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
10
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
10

Otherwise Unclassified Properties

Base Metal Price, % relative 32
30
Density, g/cm3 8.0
8.6
Embodied Carbon, kg CO2/kg material 5.4
2.8
Embodied Energy, MJ/kg 77
45
Embodied Water, L/kg 190
330

Common Calculations

Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 19
15 to 33
Strength to Weight: Bending, points 18
15 to 26
Thermal Diffusivity, mm2/s 3.1
11
Thermal Shock Resistance, points 13
17 to 36

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
2.5 to 3.1
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 20
0
Cobalt (Co), % 0
0.25 to 0.55
Copper (Cu), % 0 to 1.0
92.4 to 95.8
Iron (Fe), % 38.3 to 48.3
0 to 0.2
Lead (Pb), % 0 to 0.0050
0 to 0.050
Manganese (Mn), % 0 to 2.0
0 to 0.1
Nickel (Ni), % 34 to 37
0 to 0.2
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.75 to 1.5
1.5 to 2.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0 to 0.025
0
Zinc (Zn), % 0
0 to 0.8
Residuals, % 0
0 to 0.5