N08330 Stainless Steel vs. C64200 Bronze

N08330 stainless steel belongs to the iron alloys classification, while C64200 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is C64200 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
14 to 35
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
42
Shear Strength, MPa 360
330 to 390
Tensile Strength: Ultimate (UTS), MPa 550
540 to 640
Tensile Strength: Yield (Proof), MPa 230
230 to 320

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Maximum Temperature: Mechanical, °C 1050
210
Melting Completion (Liquidus), °C 1390
1000
Melting Onset (Solidus), °C 1340
980
Specific Heat Capacity, J/kg-K 480
430
Thermal Conductivity, W/m-K 12
45
Thermal Expansion, µm/m-K 16
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
8.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 32
29
Density, g/cm3 8.0
8.3
Embodied Carbon, kg CO2/kg material 5.4
3.0
Embodied Energy, MJ/kg 77
50
Embodied Water, L/kg 190
370

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
73 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 140
240 to 470
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 19
18 to 21
Strength to Weight: Bending, points 18
18 to 20
Thermal Diffusivity, mm2/s 3.1
13
Thermal Shock Resistance, points 13
20 to 23

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
6.3 to 7.6
Arsenic (As), % 0
0 to 0.15
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0 to 1.0
88.2 to 92.2
Iron (Fe), % 38.3 to 48.3
0 to 0.3
Lead (Pb), % 0 to 0.0050
0 to 0.050
Manganese (Mn), % 0 to 2.0
0 to 0.1
Nickel (Ni), % 34 to 37
0 to 0.25
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.75 to 1.5
1.5 to 2.2
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0 to 0.025
0 to 0.2
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0
0 to 0.5