N08330 Stainless Steel vs. C86800 Bronze

N08330 stainless steel belongs to the iron alloys classification, while C86800 bronze belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is C86800 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
22
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 76
42
Tensile Strength: Ultimate (UTS), MPa 550
570
Tensile Strength: Yield (Proof), MPa 230
260

Thermal Properties

Latent Heat of Fusion, J/g 310
180
Maximum Temperature: Mechanical, °C 1050
140
Melting Completion (Liquidus), °C 1390
900
Melting Onset (Solidus), °C 1340
880
Specific Heat Capacity, J/kg-K 480
400
Thermal Expansion, µm/m-K 16
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
9.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
10

Otherwise Unclassified Properties

Base Metal Price, % relative 32
24
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.4
3.0
Embodied Energy, MJ/kg 77
51
Embodied Water, L/kg 190
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
100
Resilience: Unit (Modulus of Resilience), kJ/m3 140
310
Stiffness to Weight: Axial, points 14
7.7
Stiffness to Weight: Bending, points 24
20
Strength to Weight: Axial, points 19
20
Strength to Weight: Bending, points 18
19
Thermal Shock Resistance, points 13
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 2.0
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0 to 1.0
53.5 to 57
Iron (Fe), % 38.3 to 48.3
1.0 to 2.5
Lead (Pb), % 0 to 0.0050
0 to 0.2
Manganese (Mn), % 0 to 2.0
2.5 to 4.0
Nickel (Ni), % 34 to 37
2.5 to 4.0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.75 to 1.5
0
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0 to 0.025
0 to 1.0
Zinc (Zn), % 0
28.3 to 40.5
Residuals, % 0
0 to 1.0