N08330 Stainless Steel vs. C93800 Bronze

N08330 stainless steel belongs to the iron alloys classification, while C93800 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is C93800 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
96
Elongation at Break, % 34
9.7
Poisson's Ratio 0.28
0.35
Shear Modulus, GPa 76
35
Tensile Strength: Ultimate (UTS), MPa 550
200
Tensile Strength: Yield (Proof), MPa 230
120

Thermal Properties

Latent Heat of Fusion, J/g 310
170
Maximum Temperature: Mechanical, °C 1050
140
Melting Completion (Liquidus), °C 1390
940
Melting Onset (Solidus), °C 1340
850
Specific Heat Capacity, J/kg-K 480
340
Thermal Conductivity, W/m-K 12
52
Thermal Expansion, µm/m-K 16
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
11
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
11

Otherwise Unclassified Properties

Base Metal Price, % relative 32
31
Density, g/cm3 8.0
9.1
Embodied Carbon, kg CO2/kg material 5.4
3.2
Embodied Energy, MJ/kg 77
51
Embodied Water, L/kg 190
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
17
Resilience: Unit (Modulus of Resilience), kJ/m3 140
70
Stiffness to Weight: Axial, points 14
5.9
Stiffness to Weight: Bending, points 24
17
Strength to Weight: Axial, points 19
6.1
Strength to Weight: Bending, points 18
8.4
Thermal Diffusivity, mm2/s 3.1
17
Thermal Shock Resistance, points 13
8.1

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.8
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0 to 1.0
75 to 79
Iron (Fe), % 38.3 to 48.3
0 to 0.15
Lead (Pb), % 0 to 0.0050
13 to 16
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 34 to 37
0 to 1.0
Phosphorus (P), % 0 to 0.030
0 to 1.5
Silicon (Si), % 0.75 to 1.5
0 to 0.0050
Sulfur (S), % 0 to 0.030
0 to 0.080
Tin (Sn), % 0 to 0.025
6.3 to 7.5
Zinc (Zn), % 0
0 to 0.8
Residuals, % 0
0 to 1.0