N08330 Stainless Steel vs. C96900 Copper-nickel

N08330 stainless steel belongs to the iron alloys classification, while C96900 copper-nickel belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is C96900 copper-nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
120
Elongation at Break, % 34
4.5
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 76
45
Tensile Strength: Ultimate (UTS), MPa 550
850
Tensile Strength: Yield (Proof), MPa 230
830

Thermal Properties

Latent Heat of Fusion, J/g 310
210
Maximum Temperature: Mechanical, °C 1050
210
Melting Completion (Liquidus), °C 1390
1060
Melting Onset (Solidus), °C 1340
960
Specific Heat Capacity, J/kg-K 480
380
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
9.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
9.2

Otherwise Unclassified Properties

Base Metal Price, % relative 32
39
Density, g/cm3 8.0
8.8
Embodied Carbon, kg CO2/kg material 5.4
4.6
Embodied Energy, MJ/kg 77
72
Embodied Water, L/kg 190
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
38
Resilience: Unit (Modulus of Resilience), kJ/m3 140
2820
Stiffness to Weight: Axial, points 14
7.7
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 19
27
Strength to Weight: Bending, points 18
23
Thermal Shock Resistance, points 13
30

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0 to 1.0
73.6 to 78
Iron (Fe), % 38.3 to 48.3
0 to 0.5
Lead (Pb), % 0 to 0.0050
0 to 0.020
Magnesium (Mg), % 0
0 to 0.15
Manganese (Mn), % 0 to 2.0
0.050 to 0.3
Nickel (Ni), % 34 to 37
14.5 to 15.5
Niobium (Nb), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.75 to 1.5
0 to 0.3
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0 to 0.025
7.5 to 8.5
Zinc (Zn), % 0
0 to 0.5
Residuals, % 0
0 to 0.5