N08330 Stainless Steel vs. Zamak 3

N08330 stainless steel belongs to the iron alloys classification, while Zamak 3 belongs to the zinc alloys. There are 32 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is N08330 stainless steel and the bottom bar is Zamak 3.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
83
Elastic (Young's, Tensile) Modulus, GPa 200
86
Elongation at Break, % 34
11
Fatigue Strength, MPa 190
48
Poisson's Ratio 0.28
0.25
Rockwell B Hardness 80
50
Shear Modulus, GPa 76
33
Shear Strength, MPa 360
210
Tensile Strength: Ultimate (UTS), MPa 550
280
Tensile Strength: Yield (Proof), MPa 230
210

Thermal Properties

Latent Heat of Fusion, J/g 310
120
Maximum Temperature: Mechanical, °C 1050
95
Melting Completion (Liquidus), °C 1390
390
Melting Onset (Solidus), °C 1340
380
Specific Heat Capacity, J/kg-K 480
410
Thermal Conductivity, W/m-K 12
110
Thermal Expansion, µm/m-K 16
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
27
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
38

Otherwise Unclassified Properties

Base Metal Price, % relative 32
11
Density, g/cm3 8.0
6.4
Embodied Carbon, kg CO2/kg material 5.4
3.0
Embodied Energy, MJ/kg 77
57
Embodied Water, L/kg 190
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 150
28
Resilience: Unit (Modulus of Resilience), kJ/m3 140
260
Stiffness to Weight: Axial, points 14
7.5
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 19
12
Strength to Weight: Bending, points 18
15
Thermal Diffusivity, mm2/s 3.1
43
Thermal Shock Resistance, points 13
8.6

Alloy Composition

Aluminum (Al), % 0
3.5 to 4.3
Cadmium (Cd), % 0
0 to 0.0050
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 17 to 20
0
Copper (Cu), % 0 to 1.0
0 to 0.25
Iron (Fe), % 38.3 to 48.3
0 to 0.1
Lead (Pb), % 0 to 0.0050
0 to 0.0050
Magnesium (Mg), % 0
0.020 to 0.060
Manganese (Mn), % 0 to 2.0
0
Nickel (Ni), % 34 to 37
0 to 0.020
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0.75 to 1.5
0 to 0.030
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0 to 0.025
0 to 0.0030
Zinc (Zn), % 0
95.3 to 96.5